1.2316ESR塑胶模具钢抚顺电渣

　　（2）供应状态和硬度淬火，估算状态前的预期，硬度2832hrc

　　（3）典型的化学成分（质量评分，％）C0.38，CR16.0抚顺电渣 ，MN0.5，SI <1.00, MO1.00对标 , Ni <1.00.

　　(4) Refer to the corresponding steel number standard steel number 1.2316ESR.

　　(5) The soft annealing specification is heated to 740-800 ° C under the protection state, and then cooled to 550 ° C at a rate of 15 ° C/h in the furnace, and then placed in the air to cool.

　　(6) The stress elimination specification must be heated to 530 ° C after rough processing.

　　(7) The first heating and recovery specifications are 540650 ° C for the first time. Or the foot pressure cooling in the vacuum furnace. R65

　　Refer to the fire curve chart to select the ignition temperature and hardness, the ignition 2 times, the recovery temperature> 180℃

　　（8）在预热的物理特性状态下：温度20°C，密度为7800g/cm3，弹性模量MPa。

　　（9）机械性能测试温度为20°C，拉伸强度为120MPa，屈服强度为980MPa，截面收缩率为47％，伸长率为12.0％。测试温度为200°C，拉伸强度为1010MPa，屈服强度为910MPa，截面收缩率为48％，伸长率为10.5％。

　　（10）典型的申请示例

　　①腐蚀性塑料模具，例如PVC和乙酸盐有没有磁性。

　　②需要在潮湿的环境中工作的塑料模具。

　　③吹塑料模具，结构零件等。